Dai Xueqian, Chen Shufen (Shanghai Institute of Organic Chemistry, Academia Sinica)
Published:
摘要: 为改善氧化锌的抗紫外辐照性能,用模数为2—3的硅酸钾对氧化锌进行包复处理,得到了软性填料PS-ZnO。其SiO_2含量大于9%,优于文献值(8%)。
关键词: 氧化锌, 填料, 硅酸盐, 表面处理
Abstract: In order to improve the stability of ZnO to UV irradiation ZnO was taeated by potassium silicate with model 2—3. Solft pigment ZnO was obtained, Its content of SiO_2 is 9% and higher than reference datum.
戴学茜,陈淑芬. 硅酸钾保护处理氧化锌填料的研究[J]. .
Dai Xueqian, Chen Shufen (Shanghai Institute of Organic Chemistry, Academia Sinica). STUDY ON TREATMENT OF ZnO BY POTASSIUM SILICATE[J]. .